| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Fadeeva, V. I.
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (1/1 displayed)
Places of action
| Organizations | Location | People |
|---|
booksection
Synthesis of powder alloys in Ni-Al-Nb-C system by mechanical alloying
Abstract
<p>Structure and phase composition of the mechanically alloyed nanocrystalline Ni-Al-Nb-C alloys with a constant content of Nb and C (5 at. % of each element) and various contents of Ni and Al were investigated. It was shown that in the alloys with C<sub>Ni</sub>/C<sub>Al</sub> = 1÷1.6, the interaction between Ni and Al, and Nb and C occurs independently because of the high negative formation enthalpies of NiAl and NbC. As a result, stable phases NiAl<sub>1-x</sub> (B2 structure) and non-stoichiometric carbide NbC<sub>x</sub> were formed during milling. When the ratio C<sub>Ni</sub>/C<sub>Al</sub>≥ 2.5, a supersaturated solid solution Ni(Al, Nb, C) with the fcc- structure was formed during the MA. Further heating up to 700°C leads to the dissociation of the solid solution; Ni<sub>3</sub>AlC<sub>x</sub> phase (Ll<sub>2</sub>) and non-stoichiometric carbide NbC<sub>x</sub> appear after the heating. The DSC curve of this alloy exhibits an exothermic effect, which corresponds to the dissociation process. Hardness was measured in pressed and sintered (700 MPa, 1200°C, 2 hours) samples; the dependence between the hardness and structure of the intermetallic matrix was found.</p>