Abstract

Modeling the longevity of marine structures is inadequate and time to ultimate failure is extremely difficult to<br/>predict. The sheer number of variables affecting the failure causes large variability in predictions. Experimental<br/>works were undertaken to further understand the rates of corrosion in submerged concrete to enhance prediction of<br/>steel section losses. This paper reports early findings from this work where CEM 1 type reinforced concrete was<br/>exposed to environments with variable oxygen concentrations. After accelerated corrosion initiation, corrosion measurements using a potentiostatic method were used to determine the average loss of steel due to corrosion. Corrosion is shown to continue to occur although the environment has a lack of oxygen. Rates are up to 50% lower exposed to oxygen concentrations of 0 to 4ppm, than in 8ppm or air exposure. These results are contradictory to common thinking suggesting that without oxygen, corrosion rates would be negligible. Further experimental works and project integration is discussed outlining future steps for the Universities of Dundee and Leeds to further reduce variability in predicting longevity off marine structures.

Topics

• impedance spectroscopy
• corrosion
• Oxygen
• steel
• low energy electron diffraction