| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Belis, Jan
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (20/20 displayed)
- 2024Experimental study on the thermal performance of soda-lime-silica glass by radiant panel testing
- 2024Experimental Work on Thick Epoxy Adhesive Bonds for Glass-Steel Joints in a Ship
- 2024Laser micromachined 3D glass photonics platform demonstrated by temperature compensated strain sensorcitations
- 2024Point-fixed connections in structural glass with injection mortar infill : experimental investigation and numerical simulationscitations
- 2024Investigation of the structural performance of continuous adhesive glass-metal connections using structural silicone and hybrid polymer adhesivescitations
- 2023Multi-physics modelling of concrete shrinkage with the lattice discrete particle model considering the volume of aggregates
- 2023Multi-physics modelling of moisture diffusion in the FRP-concrete adhesive jointscitations
- 2023Probability density function models for float glass under mechanical loading with varying parameterscitations
- 2022Experimental strength characterisation of thin chemically pre-stressed glass based on laser-induced flawscitations
- 2022Experimental investigation into the effect of elevated temperatures on the fracture strength of soda-lime-silica glasscitations
- 2021Effect of loading rate, surface flaw length and orientation on strength of laser-modified architectural glass
- 2019Architectural Glasscitations
- 2018Experimental investigation into the effects of membrane action for continuous reinforced glass beam systemscitations
- 2013Ratio of mirror zone depth to flaw depth after failure of glass beams
- 2013Experimental assessment of polymers in glass constructions
- 2013Stress corrosion parameters for glass with different edge finishing
- 2013Thermal breakage of glass
- 2011Development of structural adhesive point-fixings
- 2011The problem of a failure criterion for glass-metal adhesive bonds
- 2009Experimental material determination of viscoelastic glass/ionomer laminates
Places of action
| Organizations | Location | People |
|---|
conferencepaper
Stress corrosion parameters for glass with different edge finishing
Abstract
The influence of stress corrosion on the edge strength becomes important when designing structural glass elements. As the load duration of the design wind load (600 s) or the design temperature load is larger than the common load duration during testing the glass edge, a strength model must be used to take into account the load duration properly. In such a model, both short term parameters (i.e. the flaw geometry and depth) and stress corrosion parameters are involved. The stress corrosion parameters strongly depend upon the environment, especially the temperature and the humidity. In this study, the latter two are kept constant, for the testing at high stress rate (50 MPa/s), to determine the short term parameters as well as for the testing at low stress rate (2 MPa/s), to determine the stress corrosion parameters. The geometry factor and the stress corrosion parameters were determined for arrised and ground edges.