• Yatim, Nor Hamidah
• Azhan, Wan Muhammad Syahmi Wan
• Rahman, Hamimah Abdul
• Rahman, Nurul Farhana Abdul

Abstract

<jats:p>In this study, ceramic foams were produced using starch consolidation casting method. This research focused on the preparation of alumina-based ceramic foam by using corn starch as a pore-forming agent. Preparation of alumina based ceramic foam is studied to observe the effect of the addition of corn starch on its physical, mechanical and morphological properties. The composition of the suspension used included 64–58 wt.% alumina, 55 wt.% deionised water and other materials, such as silica and polyethylene glycol (PEG), were used as additive and dispersing agent respectively. Corn starch was added at 4, 6, 8 and 10 wt.%. The samples were preheated for gelation and coagulation processes, then dried and sintered at 1250 °C for 2 h. The ceramic foam gave a linear shrinkage from 1.07% to 3.39%. The obtained flexural strength was between 0.594 and 1.996 MPa. The average total porosity ranged from 54.05% to 70.70%. This study found that the suitable amount of corn starch in alumina foam is 4 wt.% because the resulting porosity values and flexural strength are appropriate for ceramic foams.</jats:p>

Topics

• impedance spectroscopy
• pore
• strength
• flexural strength
• casting
• forming
• porosity
• ceramic
• gelation