| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Mohamad Juoi, Jariah
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (2/2 displayed)
Places of action
| Organizations | Location | People |
|---|
article
Characterization of TiAlBN nanocomposite coating deposited via radio frequency magnetron sputtering using single hot-pressed target
Abstract
TiAlBN coatings have been deposited at varying bias voltage of 0, -60, and-150 V by radio frequency (RF) magnetron sputtering technique. A single hot-pressed Ti-Al-BN target was used for the deposition process. With glancing angle X-ray diffraction analysis (GAXRD), the nanocrystalline (nc-) (Ti,Al)N phase was identified. In addition, the existence of BN and TiB2 amorphous (a-) phase were detected by X-ray photoelectron spectroscopy (XPS) analysis. Thus, the deposited TiAlBN coatings were confirmed as nc-(Ti,Al)N/a-BN/a-TiB2 nanocomposite. On the other hand, it was found that optimum bias voltage used in present study is-60 V where the deposited TiAlBN coating exhibits an excellent adhesion quality. The adhesion quality of the coatings deposited at-60V bias voltage is classified as HF 1 evaluated using the Rockwell-C adhesion test method (developed by the Union of German Engineers).