693.932 PEOPLE
| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Gavras, Serge
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (6/6 displayed)
- 2019In situ synchrotron diffraction analysis of Zn additions on the compression properties of NK30citations
- 2018Phase formation during solidification of Mg-Nd-Zn alloyscitations
- 2018Intermetallic phase characteristics in the Mg–Nd–Zn systemcitations
- 2018The effect of Zn content on the mechanical properties of Mg-4Nd-xZn Alloys (x = 0, 3, 5 and 8 wt.%)citations
- 2017Effect of the Zn content on the compression behaviour of Mg5Nd(Zn)citations
- 2017Effect of the Zn Content on the Compression Behaviour of $mathrm{Mg_{5}}$Nd(Zn): An In Situ Synchrotron Radiation Diffraction Studycitations
Places of action
| Organizations | Location | People |
|---|
article
Phase formation during solidification of Mg-Nd-Zn alloys
Abstract
<p>Mg-4Nd base alloys with Zn additions of 3, 5 and 8 wt % were investigated with in situ synchrotron radiation diffraction during solidification. This method enabled the investigation of phase formation and transformation in the alloys. The diffraction results were supported with TEM observations on the as-solidified samples. The results show the effect of increased Zn addition on stabilizing the Mg<sub>3</sub>RE phase (RE-rare earth). The experimental results agree only partially with the theoretical calculations indicating the need to improve the existing thermodynamic database on the alloy system.</p>