• Alhamdi, Ismail

Abstract

<jats:p>Fe-Mn-Al-Ni is an Fe-based shape memory alloy (SMA) featuring higher stability and low temperature dependency of superelasticity stress over a wide range of temperatures. Additive manufacturing (AM) is a promising technique for fabricating Fe-SMA with enhanced properties, which can eliminate the limitations associated with conventional fabrication and allow for the manufacture of complicated shapes with only a single-step fabrication. The current work investigates the densification behavior and fabrication window of an Fe-Mn-Al-Ni SMA using laser powder bed fusion (LPBF). Experimental optimization was performed to identify the optimum processing window parameters in terms of laser power and scanning speed to fabricate Fe-Mn-Al-Ni SMA samples. Laser remelting was also employed to improve the characteristics of Fe-Mn-Al-Ni-fabricated samples. Characterization and testing techniques were carried out to assess the densification behavior of Fe-Mn-Al-Ni to study surface roughness, density, porosity, and hardness. The findings indicated that using a laser power range of 175–200 W combined with a scanning speed of 800 mm/s within the defined processing window parameters can minimize the defects with the material and lead to decreased surface roughness, lower porosity, and higher densification.</jats:p>

Topics

• density
• impedance spectroscopy
• surface
• hardness
• selective laser melting
• defect
• porosity
• densification