• Alqahtani, Mohammed A.
• Jeaidi, Zaid A. Al
• Rodrigues, Flavia P.
• Alrahlah, Ali A.

Abstract

<p>The bond strength of universal adhesives to air-abraded zirconia ceramic was evaluated. Overall, 40 zirconia ceramic blocks with dimensions of 6 x 6 x 4 mm were cut from pre-sintered blanks. The sintered blocks were embedded in self-cured acrylic resin. The zirconia blocks were then randomly allocated to four groups (n = 10) in which different universal adhesives were used, except for the control group in which no universal adhesive was used. A silicon mold was used to build the resin cement. All specimens were stored in distilled water for 24 h at 37 degrees C and mounted on a universal testing machine. They were then subjected to shear bond strength testing at a cross-speed of 0.5 mm/min until failure occurred. The failure modes were analyzed using a digital microscope at 50x magnification. Univariate one-way analysis of variance and Tukey's post-hoc test were used for statistical analysis. Compared with the control group, the groups with universal adhesives showed statistically significant differences (P &lt; 0.05). In addition, there was no statistically significant difference in the bond strengths of the groups with universal adhesives (P &gt; 0.05). After 24 h of storage, the cementation bond to air-abraded zirconia ceramic was improved by the application of a universal adhesive.</p>

Topics

• strength
• cement
• Silicon
• ceramic
• resin