| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Ramesh, K.
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (5/5 displayed)
- 2016Poly(methyl methacrylate-co-butyl acrylate-co-acrylic acid): Physico-chemical characterization and targeted dye sensitized solar cell applicationcitations
- 2014Effect of Silver Nanoparticles on the Mechanical and Physical Properties of Epoxy Based Silane Coupling Agentcitations
- 2014Scratch resistance enhancement of 3-glycidyloxypropyltrimethoxysilane coating incorporated with silver nanoparticlescitations
- 2004Influence of microstructure on ultraprecision grinding of cemented carbidescitations
- 2004Ultraprecision grinding of tungsten carbide for spherical mirrorscitations
Places of action
| Organizations | Location | People |
|---|
article
Scratch resistance enhancement of 3-glycidyloxypropyltrimethoxysilane coating incorporated with silver nanoparticles
Abstract
An effective method to enhance scratch resistance was developed using a 3-glycidyloxyproplytrimethoxysilane as a base on the formation of a transparent coating on glass substrate. The addition of silver nanoparticles improves further the scratch hardness of the thin film coating. The critical load obtained from the microscratch test increases from 2931 to 3319 mN upon the addition of silver nanoparticles. The size of silver nanoparticle was analysed using transmission electron microscope (TEM) and was found to be in the range of 20–40 nm. Addition of silver nanoparticles also increases the surface energy; hence the result enhances the hydrophobicity compared to substrate with only GLYMO coated on it.