| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Ruben, R. Ben
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (1/1 displayed)
Places of action
| Organizations | Location | People |
|---|
article
Identifying the Effect of PWHT on Strength of Laser Beam Welding Joints of AA2024 Aluminum Alloy
Abstract
<jats:title>Abstract</jats:title><jats:p>The corrosion-resistant and strength-to-weight ratios are the primary factors in high-strength aluminum alloy. Hence, the AA2024 alloy is a possible candidate in the critical structural fabrication industry. The traditional joining method is ineffective for welding aluminum alloys. Higher melting point and temperature variations cause alloy isolation; porosity and hot cracking are caused by melting point variations. As a result, to fabricate joints, a light heat source laser beam was used. The weaker area of most fusion-welded joints was the heat-affected zone (HAZ). The post-weld heat treatment was used at HAZ to improve the properties. According to the experimental findings, the joint welded with solution treatment and artificial aging had a maximum tensile strength of 358 MPa. Re-precipitation of precipitates may accomplish in HAZ.</jats:p>