• Garmaroudi, Zahra Andaji
• Mohammadi, Mohammadreza

Abstract

<p>The plasmonic effects of infiltrated silver (Ag) nanoparticles, with different contents, inside a nanostructured TiO₂ film on the photovoltaic performance of dye-sensitized solar cells (DSSCs) are explored. The synthesized Ag nanoparticles are immobilized onto deposited TiO₂ nanoparticles by a new strategy using 3-mercaptopropionic acid (MPA), a bifunctional linker molecule. Transmission electron microscope (TEM) images show that monodispersed Ag and polydispersed TiO₂ nanoparticles have an average diameter of 12 ± 3 nm and 5 ± 1 nm, respectively. Moreover, Fourier transform infrared spectroscopy (FTIR) analysis reveals that Ag nanoparticles were successfully functionalized and capped with MPA. Optical studies on the MPA-capped Ag nanoparticles inside TiO₂ film show an increase in the total absorbance of the electrode. Moreover, EIS measurements confirm that MPA-capped Ag nanoparticles inhibit the charge recombination and improve the stability of nanoparticles in I₃^-/I^- electrolyte. The DSSC assembled with optimal content of MPA-capped Ag nanoparticles demonstrated an enhanced power conversion efficiency (8.82% ± 0.07%) compared with the pure TiO₂ (7.30% ± 0.05%). The increase in cell efficiency was attributed to the enhanced dye light absorption in strength and spectral range due to the surface plasmon resonance of MPA-capped Ag nanoparticles in the photoanode.</p>

Topics

• nanoparticle
• surface
• silver
• strength
• transmission electron microscopy
• electrochemical-induced impedance spectroscopy
• Fourier transform infrared spectroscopy
• power conversion efficiency