• Champagnon, Bernard
• De Ligny, Dominique
• Martinet, Christine
• Cornet, Antoine
• Martinez, Valérie

Abstract

<jats:p>Densified SiO2 glasses, obtained from different pressure and temperature routes, have been annealed over a wide range of temperatures far below the glass transition temperature (500 °C-900 °C). Hot and cold compressions were useful to separate the effects of pressure and the compression temperature. In situ micro-Raman spectroscopy was used to follow the structural evolution during the thermal relaxation. A similar glass structure between the non-densified silica and the recovered densified silica after the temperature annealing demonstrates a perfect recovery of the non-densified silica glass structure. While the density decreases monotonically, the structural relaxation takes place through a more complex mechanism, which shows that density is not a sufficient parameter to fully characterize the structure of densified silica glass. The relaxation takes place through a transitory state, consisting in an increase of the network inhomogeneity, shown by an increase in the intensity of the D2 band which is associated with 3 membered rings. The activation energy of these processes is 255 ± 45 kJ/mol for the hot compressed samples. The kinetic is overall faster for the cold compressed samples. In that last case, the relaxation is partially activated by internal stresses release.</jats:p>

Topics

• density
• impedance spectroscopy
• glass
• glass
• glass transition temperature
• annealing
• activation
• Raman spectroscopy