Abstract

<jats:p>The microstructures, tensile properties, and fatigue lives of the forged Ti-17 using a 1500-ton forging simulator subjected to different solution treatments and a common aging treatment under both load- and strain-controlled conditions to evaluate high cycle fatigue and low cycle fatigue lives, respectively were examined. Then, the tensile properties, microstructures, and relationships between fatigue lives and the microstructural factors were discussed.</jats:p> <jats:p>The fatigue limit under load-controlled conditions increases with increasing solution treatment temperature up to 1143 K, which is in the (α + β) region. However, it decreases with further increase in the solution treatment temperature to 1203 K in the b region. The fatigue ratio at fatigue limit is increasing with decreasing solution treatment temperature, namely increasing the volume fraction of the primary α phase, and it relates well qualitatively with the volume fraction of the primary α phase when the solution treatment temperature is less than the b transus temperature. The fatigue life under strain-controlled conditions to evaluate the low cycle fatigue life increases with decreasing solution treatment temperature, namely increasing the volume fraction of the primary α phase. The fatigue life under strain-controlled conditions to evaluate the low cycle fatigue life relates well quantitatively with the tensile true strain at breaking of the specimen and the volume fraction of the primary α phase for each total strain range.</jats:p>

Topics

• impedance spectroscopy
• microstructure
• phase
• laser emission spectroscopy
• fatigue
• aging
• forging
• aging