| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Awais, Muhammad
University of Birmingham
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (4/4 displayed)
- 2024Development of anisotropic Nd-Fe-B powder from isotropic gas atomized powdercitations
- 2020Limitations in grain boundary processing of the recycled HDDR Nd-Fe-B systemcitations
- 2020The extraction of NdFeB magnets from automotive scrap rotors using hydrogencitations
- 2019Coercivity increase of the recycled HDDR Nd-Fe-B powders doped with DyF3 and processed via Spark Plasma Sintering & the effect of thermal treatmentscitations
Places of action
| Organizations | Location | People |
|---|
article
Development of anisotropic Nd-Fe-B powder from isotropic gas atomized powder
Abstract
This work presents an innovative approach to obtain anisotropic Nd-Fe-B powder from isotropic gas atomized powder. The new process was developed using a ternary Nd-Fe-B alloy, without the requirement for additional heavy rare earth or other critical raw materials. It comprises the following steps: (a) gas atomization to produce a polycrystalline isotropic powder; (b) annealing at high temperature to induce grain growth; (c) hydrogen decrepitation to obtain a monocrystalline powder; and (d) hydrogenation-disproportionation-desorption-recombination to obtain the final ultrafine anisotropic particles. The final particle shape is polygonal, which should improve the injection molding characteristics of current powder. The final powder exhibits both high remanence (0.97 T) and coercivity (1354 kA/m) for laboratory batch sizes, which is a result of its anisotropic ultrafine microstructure. Thus, gas atomization is considered a feasible alternative to casting methods as a first step to produce powders for anisotropic bonded magnet.