| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Ahmed, Shahroz
Tampere University
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (10/10 displayed)
- 2024Effect of Cooling Practice on the Mechanical Properties of Medium-Manganese Aluminum-Alloyed Steels after Intercritical Annealing Quench and Partition Treatmentcitations
- 2023The effect of scrap originating trace elements on the properties of low alloyed steelscitations
- 2023Effects of strain rate and adiabatic heating on mechanical behavior of medium manganese Q&P steelscitations
- 2022Quenching and partitioning response of vanadium microalloyed TRIP-assisted steel
- 2022Occurrence of dynamic strain aging in intercritically annealed low carbon high aluminum medium manganese steelscitations
- 2022Directed energy deposition of AA7075 - effect of TiC nanoparticles on microstructurecitations
- 2022Directed energy deposition of AA7075 - effect of TiC nanoparticles on microstructurecitations
- 2022Dynamic strain aging in multiphase steels
- 2020Processing map for controlling microstructure and unraveling various deformation mechanisms during hot working of CoCrFeMnNi high entropy alloycitations
- 2019Hardfaced wear resistant coatings for mining tools
Places of action
| Organizations | Location | People |
|---|
article
Occurrence of dynamic strain aging in intercritically annealed low carbon high aluminum medium manganese steels
Abstract
Medium manganese steel grades heat treated with the quench and partition (Q&P) treatment have shown promising results of strength and formability, but the number of studies on high aluminum medium manganese Q&P steels still remains rather limited. Consequently, this study investigates the mechanical properties, behavior and microstructures of a low carbon-high aluminum medium manganese (3%) steel after intercritical annealing and subsequent Q&P heat treatments with varying heat treatment parameters. Samples that were intercritically annealed above 760°C showed an ultimate tensile strength (UTS) of around 1500 MPa with uniform elongation values of approximately 10 %. On the other hand, the samples annealed at 740°C showed somewhat lower UTS values (in the range of 1000...1200 MPa) but much higher uniform and total elongations, i.e., considerably improved formability. However, the stress-strain curves of the samples annealed at 740°C showed rather severe serrations that can be connected to the dynamic strain aging (DSA) phenomenon, which limits the usability of the steel especially in applications where good surface quality of the deformed (sheet) is required. Therefore, the main focus of this article is on the samples annealed at temperatures close to A1, where DSA serrations tend to appear. The evidence gathered from these investigations leads to the conjecture that the DSA serrations are due to the free carbon and nitrogen originating from the dissolution of M(C,N) and M2(C,N) type carbides, which were formed during the intercritical annealing at temperatures producing less than 50 percent of the austenite phase. Other reasons for the occurrence of DSA in the current test materials can be the scarcity of martensite and the morphology of the retained austenite.