People | Locations | Statistics |
---|---|---|
Naji, M. |
| |
Motta, Antonella |
| |
Aletan, Dirar |
| |
Mohamed, Tarek |
| |
Ertürk, Emre |
| |
Taccardi, Nicola |
| |
Kononenko, Denys |
| |
Petrov, R. H. | Madrid |
|
Alshaaer, Mazen | Brussels |
|
Bih, L. |
| |
Casati, R. |
| |
Muller, Hermance |
| |
Kočí, Jan | Prague |
|
Šuljagić, Marija |
| |
Kalteremidou, Kalliopi-Artemi | Brussels |
|
Azam, Siraj |
| |
Ospanova, Alyiya |
| |
Blanpain, Bart |
| |
Ali, M. A. |
| |
Popa, V. |
| |
Rančić, M. |
| |
Ollier, Nadège |
| |
Azevedo, Nuno Monteiro |
| |
Landes, Michael |
| |
Rignanese, Gian-Marco |
|
Hofinger, Matthias
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (4/4 displayed)
- 2021Influence of thermomechanical fatigue loading conditions on the nanostructure of secondary hardening steelscitations
- 2020Material behaviour of a dual hardening steel under thermomechanical loadingcitations
- 2019Microstructural evolution of a dual hardening steel during heat treatmentcitations
- 2019Thermomechanical fatigue testing of dual hardening tool steelscitations
Places of action
Organizations | Location | People |
---|
article
Microstructural evolution of a dual hardening steel during heat treatment
Abstract
<p>Dual hardening steels combine precipitation of both secondary hardening carbides and intermetallic phases in a martensitic matrix. Due to this combination, the carbon content necessary to achieve high hardness levels can be reduced, resulting in a decreased amount of large and embrittling carbides. In this study, the influence of different heat treatments on microstructure evolution and secondary hardness is investigated. Different metallographic preparation methods were tested in order to visualize the microstructure. Carbides were characterized using spot-pattern electron backscatter diffraction. For light optical investigations, preparation with V2A-pickle lead to the best results. Preparation with colloidal silica suspension achieved the best results for investigations by scanning electron microscopy and for carbide characterization using electron backscatter diffraction. It was found that a homogenization treatment prior to austenitization was unable to increase the amount of dissolved carbides, and thus had no effect on secondary hardness. By increasing the austenitization temperature, the amount of carbides and secondary hardness could be increased significantly.</p>