People | Locations | Statistics |
---|---|---|
Naji, M. |
| |
Motta, Antonella |
| |
Aletan, Dirar |
| |
Mohamed, Tarek |
| |
Ertürk, Emre |
| |
Taccardi, Nicola |
| |
Kononenko, Denys |
| |
Petrov, R. H. | Madrid |
|
Alshaaer, Mazen | Brussels |
|
Bih, L. |
| |
Casati, R. |
| |
Muller, Hermance |
| |
Kočí, Jan | Prague |
|
Šuljagić, Marija |
| |
Kalteremidou, Kalliopi-Artemi | Brussels |
|
Azam, Siraj |
| |
Ospanova, Alyiya |
| |
Blanpain, Bart |
| |
Ali, M. A. |
| |
Popa, V. |
| |
Rančić, M. |
| |
Ollier, Nadège |
| |
Azevedo, Nuno Monteiro |
| |
Landes, Michael |
| |
Rignanese, Gian-Marco |
|
Thomas, Rhys
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (37/37 displayed)
- 2024Quantifying cracking and strain localisation in a cold spray chromium coating on a zirconium alloy substrate under tensile loading at room temperaturecitations
- 2024Quantifying cracking and strain localisation in a cold spray chromium coating on a zirconium alloy substrate under tensile loading at room temperaturecitations
- 2024Identification, classification and characterisation of hydrides in Zr alloyscitations
- 2024Identification, classification and characterisation of hydrides in Zr alloys
- 2024Fractional densities and character of dislocations in different slip modes from powder diffraction patternscitations
- 2024Fractional densities and character of dislocations in different slip modes from powder diffraction patternscitations
- 2024Development of novel carbon-free cobalt-free iron-based hardfacing alloys with a hard π-ferrosilicide phase
- 2024Development of novel carbon-free cobalt-free iron-based hardfacing alloys with a hard π-ferrosilicide phase
- 2023Characterization of Irradiation Damage Using X-Ray Diffraction Line-Profile Analysiscitations
- 2023Characterization of Irradiation Damage Using X-Ray Diffraction Line-Profile Analysiscitations
- 2023Exploring the hydride-slip interaction in zirconium alloyscitations
- 2023Characterization of Hydride Precipitation and Reorientation in Zircaloy-4 at Different Metallurgical States
- 2023The role of hydrides and precipitates on the strain localisation behaviour in a zirconium alloycitations
- 2023Dislocation density transients and saturation in irradiated zirconiumcitations
- 2023Dislocation density transients and saturation in irradiated zirconiumcitations
- 2022Investigating Irradiation Creep of Zircaloy-4 Using In-Situ Proton Irradiation and Transmission Electron Microscopy
- 2022Multi-dimensional study of the effect of early slip activity on fatigue crack initiation in a near-α titanium alloycitations
- 2022A novel method for radial hydride analysis in zirconium alloys:HAPPycitations
- 2022A novel method for radial hydride analysis in zirconium alloyscitations
- 2022Optimising large-area crystal orientation mapping of nanoscale β phase in α + β titanium alloys using EBSDcitations
- 2022Simulation of crystal plasticity in irradiated metals: a case study on Zircaloy-4citations
- 2022CHARACTERISATION OF HYDRIDE PRECIPITATION AND REORIENTATION IN ZIRCALOY-4 AT DIFFERENT METALLURGICAL STATES
- 2022Slip activity during low-stress cold creep deformation in a near-α titanium alloycitations
- 2022Slip activity during low-stress cold creep deformation in a near-α titanium alloycitations
- 2021The Effect of Loading Direction on Slip and Twinning in an Irradiated Zirconium Alloycitations
- 2021Understanding the role of local texture variation on slip activity in a two-phase titanium alloycitations
- 2021Understanding the role of local texture variation on slip activity in a two-phase titanium alloycitations
- 2020Comparison of sub-grain scale digital image correlation calculated using commercial and open-source software packagescitations
- 2020Understanding strain localisation behaviour in a near-α Ti-alloy during initial loading below the yield stress
- 2020Early slip activity and fatigue crack initiation of a near alpha titanium alloycitations
- 2019Characterisation of irradiation enhanced strain localisation in a zirconium alloycitations
- 2019Characterisation of irradiation enhanced strain localisation in a zirconium alloycitations
- 2019Identification of active slip mode in a hexagonal material by correlative scanning electron microscopycitations
- 2019Identification of active slip mode in a hexagonal material by correlative scanning electron microscopycitations
- 2019Data for: Characterisation of irradiation enhanced strain localisation in a zirconium alloy
- 2018Enabling high resolution strain mapping in zirconium alloyscitations
- 2018Enabling high resolution strain mapping in zirconium alloyscitations
Places of action
Organizations | Location | People |
---|
article
Optimising large-area crystal orientation mapping of nanoscale β phase in α + β titanium alloys using EBSD
Abstract
α + β titanium alloys, such as the commercially important alloy Ti-6Al-4 V (Ti64), develop complex textures during thermomechanical processing due to the allotropic phase transformation between the β and α phases. These phases are crystallographically related through the Burgers orientation relationship (BOR) and are often characterised by electron backscatter diffraction (EBSD) in the scanning electron microscope (SEM). However, the BOR can be destroyed for the primary α in wrought Ti64, and techniques that utilise the BOR to reconstruct the β phase from the room temperature α-phase data cannot be used. Instead, the β texture must be measured from the residual, nanoscale β ligaments in the room temperature microstructure, which are challenging to index because of orientation and phase overlap in the EBSD Kikuchi patterns. In this work, the SEM-EBSD acquisition and processing parameters were systematically varied to determine how best to index the residual β in Ti64, and an experimental methodology was thus developed to measure the β-phase texture efficiently and reliably after thermomechanical processing. The best compromise for maximising indexing of the residual β was achieved with a low current (~1 nA in this case), and additional indexing was achieved by increasing the sample stage tilt (to 75° in this case) and by limited the scanning frame size. It was shown that the β-phase texture could be reliably measured with the optimised beam and tilt settings using a relatively coarse step size (3 μm), but this approach does not yield any morphological or spatially relevant microstructure data. Thus, it was proposed that numerous multi-scale scans be performed with different settings to characterise the residual β phase in T64, each optimised to acquire either bulk texture analysis or microstructure spatial and morphological detail.