| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Szota, M.
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (4/4 displayed)
- 2016Analysis of the Thermal and Magnetic Properties of Amorphous Fe 61Co10Zr2.5Hf2.5Me2W2B20 (Where Me = Mo, Nb, Ni Or Y) Ribbonscitations
- 2016Characterization of three-dimensional printed composite scaffolds prepared with different fabrication methodscitations
- 2013Investigation of magnetic properties of Fe 61Co8Zr4−xY2+xNi5Nb5B15 amorphous alloys (x = 0, 1) in the form of ribbonscitations
- 2010Influence of structural defects on the magnetization process in high-magnetic fields in the Fe61Co10Y8Nb1B20 alloy in the form of ribbons and platescitations
Places of action
| Organizations | Location | People |
|---|
article
Influence of structural defects on the magnetization process in high-magnetic fields in the Fe61Co10Y8Nb1B20 alloy in the form of ribbons and plates
Abstract
Amorphous samples of the Fe61Co10Y8Nb1B20 alloy in the form of a ribbon with thickness of approximately 30 mm and in the form of a plate with thickness of 0.5 mm have been investigated. Plates were obtained by a suction-casting method, and ribbons by a single roller melt-spinning method. Microstructural studies, using X-ray spectroscopy, confirmed that samples in the as-quenched state were fully amorphous. Measurements carried out using a vibrating sample magnetometer allowed values of coercivity and saturation magnetization to be obtained; it also facilitated the estimation of size and nature of structural defects in the investigated samples. All of the investigated samples of this alloy in the as-quenched state have high values of saturation magnetization of greater than 1.25 T.