693.932 PEOPLE
| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Takahashi, Minoru
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (6/6 displayed)
- 2011Flow Assisted Corrosion and Erosion-Corrosion of RAFM Steel in liquid breederscitations
- 2011Corrosion resistance of ceramics SiC and Si3N4 in flowing lead-bismuth eutecticcitations
- 2006Corrosion of steels with surface treatment and Al-alloying by GESA exposed in lead–bismuthcitations
- 2005METALLURGICAL STUDY ON ELECTRO-MAGNETIC FLOW METER AND PUMP FOR LIQUID LEAD-BISMUTH FLOWcitations
- 2005Metallurgical study on erosion and corrosion behaviors of steels exposed to liquid lead–bismuth flowcitations
- 2005Metallurgical Analysis of a Tube Ruptured in the Lead Bismuth Corrosion Test Facility
Places of action
| Organizations | Location | People |
|---|
article
Flow Assisted Corrosion and Erosion-Corrosion of RAFM Steel in liquid breeders
Abstract
Corrosion experiments for RAFM, JLF-1 steel (Fe–9Cr–2W–0.1C) in three types of liquid breeders (i.e. Li, Pb–17Li and Flinak) were performed at 600 ◦ C. The influence of the different experimental parameters, such as a flowing condition, an exposure time and a geometric condition, on the corrosion behavior was investigated. The present study focused on the evaluation of the weight loss of the corroded specimen by the corrosion model based on mass transfer. The dissolution of the metal elements from the steel was accelerated by the fluids. An erosion–corrosion of the steel was caused by the peeling off of the corroded steel surface in the flowing liquid breeders.