693.932 PEOPLE
| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Tsisar, Valentyn
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (15/15 displayed)
- 2024Early stages of liquid-metal corrosion on pre-oxidized surfaces of austenitic stainless steel 316L exposed to static Pb-Bi eutectic at 400 °C
- 2022Effect of variation in oxygen concentration in static Pb–Bi eutectic on long-term corrosion performance of Al-alloyed austenitic steels at 500 °Ccitations
- 2021Effect of oxygen concentration in static Pb–Bi eutectic on corrosion mode of aluminum-alloyed austenitic steels at 550°C for 1000 h
- 2019Corrosion in Iron and Steel T91 Caused by Flowing Lead–Bismuth Eutectic at 400 °C and 10−7 Mass% Dissolved Oxygencitations
- 2018Corrosion in aluminium-alloyed austenitic steel caused by static lead-bismuth eutectic: Effect of dissolved oxygen concentration after exposure for 1000 h at 550⁰C
- 2018Effect of oxygen concentration in static Pb at 700⁰C and Pb-Bi eutectic at 550⁰C on corrosion behavior of aluminium-alloyed austenitic steels
- 2018Effect of Structural State and Surface Finishing on Corrosion Behavior of 1.4970 Austenitic Steel at 400 and 500 °C in Flowing Pb-Bi Eutectic With Dissolved Oxygencitations
- 2017Effect of structural state of austenitic steel 15-15 Ti on initiation and propagation of solution-based corrosion attack in flowing liquid Pb-Bi eutectic at 400 and 500⁰C
- 2011THE CORROSION INFLUENCE OF PB-LI ON MICROSTRUCTURE AND MECHANICAL PROPERTIES
- 2011Flow Assisted Corrosion and Erosion-Corrosion of RAFM Steel in liquid breederscitations
- 2011Mass transfer of RAFM steel in Li by simple immersion, impeller induced flow and thermal convectioncitations
- 2011Effect of Nitrogen on the Corrosion Behavior of RAFM JLF-1 Steel in Lithiumcitations
- 2010Phase-structural transformations in the RAF/M, F/M and model F/ODS steels exposed to lithium - corrosion induced coarsening of substructure and effect of alloying elementscitations
- 2010Corrosion of reduced activation ferritic martensitic steel JLF-1 in purified Flinak at static and flowing conditionscitations
- 2010Erosion-corrosion of RAFM JLF-1 steel in lithium flow induced by impeller
Places of action
| Organizations | Location | People |
|---|
article
Flow Assisted Corrosion and Erosion-Corrosion of RAFM Steel in liquid breeders
Abstract
Corrosion experiments for RAFM, JLF-1 steel (Fe–9Cr–2W–0.1C) in three types of liquid breeders (i.e. Li, Pb–17Li and Flinak) were performed at 600 ◦ C. The influence of the different experimental parameters, such as a flowing condition, an exposure time and a geometric condition, on the corrosion behavior was investigated. The present study focused on the evaluation of the weight loss of the corroded specimen by the corrosion model based on mass transfer. The dissolution of the metal elements from the steel was accelerated by the fluids. An erosion–corrosion of the steel was caused by the peeling off of the corroded steel surface in the flowing liquid breeders.