| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Díaz, Belén
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (4/4 displayed)
- 2022Two and four–electrode configurations for contactless reinforced concrete corrosion monitoringcitations
- 2014Interface control of atomic layer deposited oxide coatings by filtered cathodic arc deposited sublayers for improved corrosion protectioncitations
- 2013Tantalum oxide nanocoatings prepared by atomic layer and filtered cathodic arc deposition for corrosion protection of steelcitations
- 2011Failure mechanism of thin Al2O3 coatings grown by atomic layer deposition for corrosion protection of carbon steelcitations
Places of action
| Organizations | Location | People |
|---|
article
Tantalum oxide nanocoatings prepared by atomic layer and filtered cathodic arc deposition for corrosion protection of steel
Abstract
A comparative study by Time-of-Flight Secondary Ions Mass Spectrometry and X-ray Photoelectron Spectroscopy, i–E polarization curves and Electrochemical Impedance Spectroscopy of the corrosion pro- tection of low alloy steel by 50 nm thick tantalum oxide coatings prepared by low temperature Atomic Layer Deposition (ALD) and Filtered Cathodic Arc Deposition (FCAD) is reported. The data evidence the presence of a spurious oxide layer mostly consisting of iron grown by transient thermal oxidation at the ALD film/substrate interface in the initial stages of deposition and its suppression by pre-treatment in the FCAD process. Carbonaceous contamination (organic and carbidic) resulting from incomplete removal of the organic precursor is the major cause of the poorer sealing properties of the ALD film. No coating dissolution is demonstrated in neutral or acid 0.2 M NaCl solutions. In acid solution localized corrosion by pitting proceeds faster with the ALD than with the FCAD coating. The roles of the pre-existing channel defects exposing the substrate surface and of the spurious interfacial oxide promoting coating breakdown and/or delamination are emphasized.