| People | Locations | Statistics |
|---|---|---|
| Naji, M. |
| |
| Motta, Antonella |
| |
| Aletan, Dirar |
| |
| Mohamed, Tarek |
| |
| Ertürk, Emre |
| |
| Taccardi, Nicola |
| |
| Kononenko, Denys |
| |
| Petrov, R. H. | Madrid |
|
| Alshaaer, Mazen | Brussels |
|
| Bih, L. |
| |
| Casati, R. |
| |
| Muller, Hermance |
| |
| Kočí, Jan | Prague |
|
| Šuljagić, Marija |
| |
| Kalteremidou, Kalliopi-Artemi | Brussels |
|
| Azam, Siraj |
| |
| Ospanova, Alyiya |
| |
| Blanpain, Bart |
| |
| Ali, M. A. |
| |
| Popa, V. |
| |
| Rančić, M. |
| |
| Ollier, Nadège |
| |
| Azevedo, Nuno Monteiro |
| |
| Landes, Michael |
| |
| Rignanese, Gian-Marco |
|
Colas, Kimberly
CEA Saclay
in Cooperation with on an Cooperation-Score of 37%
Topics
Publications (15/15 displayed)
- 2022Environmental degradation of nuclear materials: the use of advanced characterization techniques to understand physical and chemical phenomena
- 2021Impact of ion and neutron irradiation on the corrosion of the 6061-T6 aluminium alloy ; Influence de l'irradiation par ions et neutrons sur la corrosion de l'alliage d'aluminium 6061-T6citations
- 2021Impact of the microstructure on the swelling of aluminum alloys: characterization and modelling basescitations
- 2021Impact of ion and neutron irradiation on the corrosion of the 6061-T6 aluminium alloycitations
- 2020Effects of temperature and pH on uniform and pitting corrosion of aluminium alloy 6061-T6 and characterisation of the hydroxide layerscitations
- 2020Effects of temperature and pH on uniform and pitting corrosion of aluminium alloy 6061-T6 and characterisation of the hydroxide layers ; Effet de la température et du pH sur la corrosion de l'alliage d'Al 6061-T6 et caractérisation des couches d'oxydescitations
- 2019Correlation between quenching rate, mechanical properties and microstructure in thick sections of Al Mg Si( Cu) alloyscitations
- 2019Effect of hardening on toughness captured by stress-based damage nucleation in 6061 aluminum alloycitations
- 2018Understanding of Corrosion Mechanisms after Irradiation: Effect of Ion Irradiation of the Oxide Layers on the Corrosion Rate of M5citations
- 2018Study of the influence of the initial pH on the aqueous corrosion of an Al-Mg-Si alloy at 70°C
- 2018Effect of ion irradiation of the metal matrix on the oxidation rate of Zircaloy-4citations
- 2018Microstructure Evolution in Ion-Irradiated Oxidized Zircaloy-4 Studied with Synchrotron Radiation Microdiffraction and Transmission Electron Microscopycitations
- 2017Stability of β″ nano-phases in Al-Mg-Si(-Cu) alloy under high dose ion irradiationcitations
- 2016Identification of monoclinic θ-phase dispersoids in a 6061 aluminium alloycitations
- 2015Influence of light ion irradiation of the oxide layer on the oxidation rate of Zircaloy-4citations
Places of action
| Organizations | Location | People |
|---|
article
Effect of ion irradiation of the metal matrix on the oxidation rate of Zircaloy-4
Abstract
The oxidation kinetics acceleration observed in Zircaloy-4 cladding in Pressurized Water Reactor could be partially due to metal irradiation damage occuring in-pile. To check this assumption, several ion irradiation tests of the Zircaloy-4 metal matrix were performed to reproduce the evolution of the metallurgical state in reactor. This study showed that the amorphization process of the intermetallic precipitates (SPPs) does not change significantly the oxidation rate of Zircaloy-4. Implantation of iron in the matrix to simulate iron dissolution from the SPPs has no real impact on the corrosion kinetics. However proton irradiations at 350 °C producing <a> dislocation loops resulted in a significant increase in the oxidation rate.